¥ 13.30
25千克起订
产品规格
可售数量: 60000千克
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | 490(6,950) | kg/cm²(MPa)[Lb/in2] | |
断裂伸长率 | ASTM D638/ISO 527 | - | |||
拉伸模量 | ASTM D638/ISO 527 | - | kg/cm²(MPa)[Lb/in2] | ||
拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | 20 | |||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | - | |||
弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 27000(38000) | kg/cm²(MPa)[Lb/in2] | ||
弯曲强度 | ASTM D790/ISO 178 | 790(11,660) | kg/cm²(MPa)[Lb/in2] | ||
洛氏硬度 | ASTM D785 | R-116 | |||
IZOD 缺口冲击强度 | 1/4" 23 | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | |
1/4" -30 | ASTM D256/ISO 179 | 17(3.1) | kg·cm/cm(J/M)ft·lb/in | ||
1/8" 23 | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
1/8" -30 | ASTM D256/ISO 179 | 20(3.7) | kg·cm/cm(J/M)ft·lb/in | ||
Charpy冲击强度 | 23 (缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | |
-30(缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
23(无缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
-30(无缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.05 | ||
成型收缩率 | ASTM D955 | - | |||
熔融指数(流动系数) | 200/5kg | ASTM D1238/ISO 1133 | 1.6 | g/10min | |
220/10kg | ASTM D1238/ISO 1133 | 23 | g/10min | ||
吸水率 23/24H | ASTM D570/ISO 62 | - | |||
热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 99(210) | |
未退火 | ASTM D648/ISO 75 | 88(190) | |||
维卡软化点 | ASTM D1525/ISO R306 | 105(221) | |||
熔点 | - | - | |||
燃烧性(率) | UL94 | 1.6mmHB | |||
线性膨胀系数 | ASTM D696/ISO 11359 | - | mm/mm. | ||
加工条件 | 干燥条件 | 80°C下烘料约23小时 | |||
加工温度 | 射嘴 | 180230°C | |||
料筒前段 | 190230 | ||||
料筒中段 | 190230 | ||||
料筒后段 | 180220 | ||||
熔体温度 | - | ||||
模具温度 | 3070°C | ||||
压力 | 注塑压力 | - | Mpa | ||
保压压力 | - | Mpa | |||
背压 | - | Mpa | |||
螺杆转速 | - | rpm | |||
其他 | 备注 | - | |||
颜色 | - | ||||
特性 | 高光泽性 高刚性。 | ||||
用途 | 电视机前壳 / 复印机外壳 / 电话机壳 / 化妆品盒 / 轮胎盖 |