Coreweld 88HS-Ni1 is recommended primarily for robotic or mechanized high speed welding of sheet steel. Welding speeds up to 90 ipm are possible when welding vertical down. The low slag level of Coreweld 88HS-Ni1 minimizes post weld clean up. For this reason, Coreweld 88HS-Ni1 gives special advantage in applications where post weld coating or painting is specified. Coreweld 88HS-Ni1 is a 1% nickel low alloy metal cored wire designed specifically for high speed welding where a clean weld surface is required. Coreweld 88HS-Ni1 deposits have very few silicon islands and almost no slag at the weld toes.

Typical Charpy V-Notch Properties

As Welded 75% Ar - 25% Co2
As Welded 90% Ar - 10% Co2

Typical Tensile Properties

Condition	As Welded	As Welded
Reduction in Area	58 %	60 %
Shielding Gas	90% Ar - 10% CO2	75% Ar - 25% CO2
Tensile Strength	598 MPa (86.7 ksi)	576 MPa (83.6 ksi)
Yield Strength	512 MPa (74.3 ksi)	480 MPa (69.6 ksi)
Elongation	26 %	27 %

Recommended Welding Parameters

Current	TTW Dist.	Voltage	Wire Diameter	Wire Feed Speed
75% Ar - 25% CO2
230-510 A	19 mm (3/4 in.)	26-36 V	1.6 mm (1/16 in.)	381-1219 mm/min (150-480 in./min)
190-410 A	15.8 mm (5/8 in.)	27-36 V	1.4 mm (.052 in.)	457-1346 cm/min (180-530 in./min)
200-360 A	15.8 mm (5/8 in.)	27-33 V	1.2 mm (.045 in.)	635-1397 mm/min (250-550 in./min)

Deposition Data

Current	Deposition Rate	Diameter	Deposition Efficiency (%)	Voltage	Wire Feed Speed
75% Ar - 25% CO2
210 A	2.4 kg/h (5.2 lb/h)	1.2 mm (.045 in.)	94 %	27 V	635 cm/min (250 in./min)
265 A	3.5 kg/h (7.7 lb/h)	1.2 mm (.045 in.)	96 %	28 V	889 cm/min (350 in./min)
295 A	4.6 kg/h (10.2 lb/h)	1.2 mm (.045 in.)	98 %	29 V	1016 cm/min (400 in./min)
330 A	5.8 kg/h (12.7 lb/h)	1.2 mm (.045 in.)	99 %	32 V	1270 cm/min (500 in./min)
375 A	7.5 kg/h (16.5 lb/h)	1.2 mm (.045 in.)	99 %	33 V	1397 cm/min (550 in./min)
190 A	2.5 kg/h (5.5 lb/h)	1.4 mm (.052 in.)	94 %	25 V	445 cm/min (175 in./min)
240 A	3.5 kg/h (7.7 lb/h)	1.4 mm (.052 in.)	95 %	27 V	635 cm/min (250 in./min)
255 A	4.9 kg/h (10.7 lb/h)	1.4 mm (.052 in.)	98 %	28 V	762 cm/min (300 in./min)
350 A	6.2 kg/h (13.6 lb/h)	1.4 mm (.052 in.)	99 %	31 V	1016 cm/min (400 in./min)
430 A	7.5 kg/h (16.6 lb/h)	1.4 mm (.052 in.)	99 %	36 V	1334 cm/min (525 in./min)
240 A	2.8 kg/h (6.2 lb/h)	1.6 mm (1/16 in.)	91 %	26 V	381 cm/min (150 in./min)
290 A	4.0 kg/h (8.8 lb/h)	1.6 mm (1/16 in.)	95 %	27 V	508 cm/min (200 in./min)
340 A	5.7 kg/h (12.5 lb/h)	1.6 mm (1/16 in.)	98 %	29 V	635 cm/min (250 in./min)
425 A	7.2 kg/h (15.9 lb/h)	1.6 mm (1/16 in.)	99 %	32 V	889 cm/min (350 in./min)
490 A	9.4 kg/h (20.7 lb/h)	1.6 mm (1/16 in.)	99 %	36 V	1207 cm/min (475 in./min)
90% Ar - 10% CO2
180 A	2.4 kg/h (5.2 lb/h)	1.2 mm (.045 in.)	94 %	23.5 V	508 cm/min (200 in./min)
250 A	3.5 kg/h (7.7 lb/h)	1.2 mm (.045 in.)	96 %	25 V	762 cm/min (300 in./min)
300 A	4.6 kg/h (10.2 lb/h)	1.2 mm (.045 in.)	98 %	27 V	1016 cm/min (400 in./min)
375 A	5.8 kg/h (12.7 lb/h)	1.2 mm (.045 in.)	99 %	29 V	1270 cm/min (500 in./min)
450 A	7.5 kg/h (16.5 lb/h)	1.2 mm (.045 in.)	99 %	32 V	1651 cm/min (650 in./min)
200 A	2.5 kg/h (5.5 lb/h)	1.4 mm (.052 in.)	94 %	24 V	445 cm/min (175 in./min)
260 A	3.5 kg/h (7.7 lb/h)	1.4 mm (.052 in.)	95 %	25 V	635 cm/min (250 in./min)
340 A	4.9 kg/h (10.7 lb/h)	1.4 mm (.052 in.)	98 %	27 V	889 cm/min (350 in./min)
420 A	6.2 kg/h (13.6 lb/h)	1.4 mm (.052 in.)	99 %	30 V	1143 cm/min (450 in./min)
450 A	7.5 kg/h (16.6 lb/h)	1.4 mm (.052 in.)	99 %	32 V	1397 cm/min (550 in./min)
240 A	2.8 kg/h (6.2 lb/h)	1.6 mm (1/16 in.)	91 %	24 V	381 cm/min (150 in./min)
310 A	4.0 kg/h (8.8 lb/h)	1.6 mm (1/16 in.)	95 %	26 V	508 cm/min (200 in./min)
400 A	5.7 kg/h (12.5 lb/h)	1.6 mm (1/16 in.)	98 %	28 V	699 cm/min (275 in./min)
440 A	7.2 kg/h (15.9 lb/h)	1.6 mm (1/16 in.)	99 %	29 V	889 cm/min (350 in./min)
515 A	9.4 kg/h (20.7 lb/h)	1.6 mm (1/16 in.)	99 %	33 V	1207 cm/min (475 in./min)