【瑞典伊萨低合金钢气保焊丝DUAL SHIELD II 100-D1自保护药芯焊丝】价格_批发_厂家_参数_图片_焊丝

1/1

瑞典伊萨低合金钢气保焊丝DUAL SHIELD II 100-D1自保护药芯焊丝

¥ 35.00

15公斤起订

产品规格

规格: 1.2mm 1.6mm

赫克托（上海）焊材有限公司

5年

经营年限

上海

所在地区

7.6

综合评分

全部产品进入店铺

图文详情

产品属性

产品信息.jpg

Dual Shield II 100-D1 is an all-position flux cored electrode specially formulated to weld quenched and tempered steels that require a postweld heat treatment using 75% Ar / 25% CO2 shielding gas. Dual Shield II 100-D1 was designed to weld oil field components made of 4130, 8630, API X-80 and similar steels.

Typical Charpy V-Notch Properties

Stress Relieved
Impact Value	20 ft-lb
Impact Value	27 J
Shielding Gas	75% Ar - 25% CO2
	1175 °F
	635 °C
	8 hr
Testing Temperature	-25 °F
Testing Temperature	-32 °C

Typical Tensile Properties

Condition	Stress Relieved	As Welded
Reduction in Area	58 %	58 %
Shielding Gas	75% Ar - 25% CO2	75% Ar - 25% CO2
Tensile Strength	650 MPa (94 ksi)	705 MPa (102 ksi)
Yield Strength	585 MPa (85 ksi)	650 MPa (94 ksi)
Elongation	26 %	23 %
Testing Time	8 hr
Testing Temperature	635 degC (1175 degF)

Recommended Welding Parameters

Current	TTW Dist.	Voltage	Wire Diameter	Wire Feed Speed
75% Ar - 25% CO2
130-200 A	9.5-12.7 mm (3/8-1/2 in.)	22-26 V	1.2 mm (.045 in.)	381-660 cm/min (150-260 in./min)
200-225 A	12.7-19 mm (1/2-3/4 in.)	24-27 V	1.2 mm (.045 in.)	660-965 cm/min (260-380 in./min)
225-265 A	19-25.4 mm (3/4-1 in.)	27-29 V	1.2 mm (.045 in.)	965-1321 cm/min (380-520 in./min)
135-250 A	12.7-16 mm (1/2-5/8 in.)	22-26 V	1.4 mm (.052 in.)	279-584 cm/min (110-230 in./min)
250-295 A	16-19 mm (5/8-3/4 in.)	25-29 V	1.4 mm (.052 in.)	584-864 cm/min (230-340 in./min)
295-355 A	19-25.4 mm (3/4-1 in.)	27-31 V	1.4 mm (.052 in.)	864-1194 cm/min (340-470 in./min)
185-285 A	16-19 mm (5/8-3/4 in.)	24-28 V	1.6 mm (1/16 in.)	279-508 cm/min (110-200 in./min)
285-340 A	19-25.4 mm (3/4-1 in.)	27-30 V	1.6 mm (1/16 in.)	508-762 cm/min (200-300 in./min)
340-400 A	25.4-31.75 mm (1-1.25 in.)	28-32 V	1.6 mm (1/16 in.)	762-1067 cm/min (300-420 in./min)

Deposition Data

Current	Deposition Rate	Diameter	Deposition Efficiency (%)	Voltage	Wire Feed Speed
75% Ar - 25% CO2
150 A	1.9 kg/h (4.2 lb/h)	1.2 mm (.045 in.)	86 %	28 V	508 cm/min (200 in./min)
210 A	2.8 kg/h (6.3 lb/h)	1.2 mm (.045 in.)	86 %	29 V	762 cm/min (300 in./min)
250 A	3.9 kg/h (8.5 lb/h)	1.2 mm (.045 in.)	87 %	30 V	1016 cm/min (400 in./min)
290 A	4.8 kg/h (10.7 lb/h)	1.2 mm (.045 in.)	87 %	33 V	1270 cm/min (500 in./min)
155 A	2.0 kg/h (4.4 lb/h)	1.4 mm (.052 in.)	87 %	25 V	381 cm/min (150 in./min)
245 A	3.3 kg/h (7.3 lb/h)	1.4 mm (.052 in.)	86 %	28 V	635 cm/min (250 in./min)
310 A	4.6 kg/h (10.2 lb/h)	1.4 mm (.052 in.)	85 %	33 V	889 cm/min (350 in./min)
360 A	6.0 kg/h (13.3 lb/h)	1.4 mm (.052 in.)	85 %	36 V	1143 cm/min (450 in./min)
430 A	8.0 kg/h (17.6 lb/h)	1.4 mm (.052 in.)	87 %	37 V	1524 cm/min (600 in./min)
190 A	2.8 kg/h (6.1 lb/h)	1.6 mm (1/16 in.)	87 %	27 V	38 cm/min (150 in./min)
300 A	4.6 kg/h (10.2 lb/h)	1.6 mm (1/16 in.)	87 %	30 V	35 cm/min (250 in./min)
365 A	5.5 kg/h (12.3 lb/h)	1.6 mm (1/16 in.)	86 %	33 V	762 cm/min (300 in./min)
410 A	6.3 kg/h (14.0 lb/h)	1.6 mm (1/16 in.)	88 %	33 V	889 cm/min (350 in./min)