Dual Shield T-115 is a basic slag flux cored electrode designed for applications requiring a high strength weld deposit. Dual Shield T-115 produces weld deposits which are resistant to cracking in heavy sections or under high restraint. It has good usability with a minimum amount of spatter and easy slag removal. It can be used for welding steels such as: T-1, HY-80, HY-90, N-A-XTRA 90, 100 and 110, and the SSS 100 series. The weld metal analysis is similar to an E11018-M low hydrogen electrode. A CO2 shielding gas is recommended for the 3/32" (2.4 mm) size and a 75% Ar / 25% CO2 gas for the .045 " (1.2 mm) and 1/16" (1.6 mm) sizes.

Typical Charpy V-Notch Properties


As Welded 75% Ar - 25% Co2
Stress Relieved 75% Ar - 25% Co2
1 hr
1 hr

Typical Tensile Properties

Condition	Stress Relieved	As Welded	As Welded
Reduction in Area	65 %	57 %	43 %
Shielding Gas	75% Ar - 25% CO2	CO2	75% Ar - 25% CO2
Tensile Strength	750 MPa (109 ksi)	662 MPa (96 ksi)	815 MPa (118 ksi)
Yield Strength	660 MPa (96 ksi)	810 MPa (117 ksi)	761 MPa (110 ksi)
Elongation	23 %	22 %	20 %
Testing Time	1 hr
Testing Temperature	566 degC (1050 degF)

Recommended Welding Parameters

Current	TTW Dist.	Voltage	Wire Diameter	Wire Feed Speed
75% Ar - 25% CO2
140-190 A	19-25.4 mm (3/4-1 in.)	19-28 V	1.2 mm (.045 in.)	635-889 cm/min (250-350 in./min)
220-280 A	19-25.4 mm (3/4-1 in.)	29-30 V	1.6 mm (1/16 in.)	457-635 cm/min (180-250 in./min)
280-380 A	25.4-31.75 mm (1-1.25 in.)	31-32 V	1.6 mm (1/16 in.)	635-1016 cm/min (250-400 in./min)
240-370 A	25.4-31.75 mm (1-1.25 in.)	30-32 V	2.4 mm (3/32 in.)	254-508 cm/min (100-200 in./min)
370-460 A	31.75-38 mm (1.25-1.5 in.)	32-33 V	2.4 mm (3/32 in.)	508-813 cm/min (200-320 in./min)
240-300 A	19-25.4 mm (3/4-1 in.)	29-32 V	1.2 mm (.045 in.)	1143-1651 cm/min (450-650 in./min)

Deposition Data

Current	Deposition Rate	Diameter	Deposition Efficiency (%)	TTW Dist.	Voltage	Wire Feed Speed
75% Ar - 25% CO2
170 A	3.2 kg/h (7.0 lb/h)	1.2 mm (.045 in.)	96 %	19 mm (3/4 in.)	19 V	724 cm/min (285 in./min)
250 A	4.9 kg/h (10.8 lb/h)	1.2 mm (.045 in.)	91 %	25.4 mm (1 in.)	30 V	1191 cm/min (469 in./min)
400 A	7.3 kg/h (16.1 lb/h)	1.6 mm (1/16 in.)	92 %	25.4 mm (1 in.)	32 V	937 cm/min (369 in./min)
300 A	6.44 kg/h (14.2 lb/h)	1.2 mm (.045 in.)	92 %	25.4 mm (1 in.)	32 V	1539 cm/min (606 in./min)
300 A	4.45 kg/h (9.8 lb/h)	1.6 mm (1/16 in.)	92 %	25.4 mm (1 in.)	30 V	574 cm/min (226 in./min)
450 A	8 kg/h (17.6 lb/h)	2.4 mm (3/32 in.)	85 %	25.4 mm (1 in.)	32 V	551 cm/min (217 in./min)
475 A	9.1 kg/h (20.0 lb/h)	2.4 mm (3/32 in.)	87 %	25.4 mm (1 in.)	32 V	622 cm/min (245 in./min)
500 A	10.3 kg/h (22.8 lb/h)	2.4 mm (3/32 in.)	89 %	25.4 mm (1 in.)	32 V	686 cm/min (270 in./min)

Classifications

ASME SFA 5.36 :
ASME SFA 5.29 :
AWS A5.36 : E111T5-M21A6-K4-H4 (.045”, .052”, 1/16”)
AWS A5.36 : E110T5-C1A6-K4-H4 (3/32")
AWS A5.29 : E110T5-K4C (3/32")
AWS A5.29 : E111T5-K4M-H4 (.045", .052", 1/16")

Approvals

Grade	CSA W48 E111T5-K4M-H4 (.045”,.052”,1/16”), E110T5-K4C-H4 (3/32”)
Society	CWB

Approvals are based on factory location. Please contact ESAB for more information.

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C	Cr	Mn	Mo	Ni	P	S	Si
CO2
0.06 %	0.44 %	1.86 %	0.44 %	2.11 %	0.011 %	0.012 %	0.56 %
75% Ar - 25% CO2
0.05 %	0.25 %	1.86 %	0.47 %	2.04 %	0.010 %	0.012 %	0.52 %