Dual Shield II 101H4M is one of a series of low hydrogen flux cored electrodes introduced by ESAB. Each of the new Dual Shield II H4 wires is an all-position flux cored electrode that provides excellent low temperature toughness in both the as welded and/or stress relieved conditions (as applicable) when used with 75% Ar/25% CO2. Each can produce diffusible hydrogen levels of < 4mL/100g deposited over a wide range of welding parameters. Dual Shield II 101H4M is especially designed to weld HY-80 and HSLA-100 steels typically used in shipbuilding. Suitable for single or multi-pass welding applications. This wire was developed to meet the stringent requirements of MIL-E-24403/2 and offshore welding, and it is an ideal choice for HSLA steels.
Typical Charpy V-Notch Properties
| As Welded 75% Ar - 25% Co2 |
Typical Tensile Properties
| Condition | As Welded | As Welded |
| AWS A5.29 Requirement | MIL-E-24403/2 Vertical-Up HY-80 Base Plate | |
| Reduction in Area | 67 % | 68 % |
| Shielding Gas | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 |
| Tensile Strength | 705 MPa (102 ksi) | 680 MPa (101 ksi) |
| Yield Strength | 640 MPa (93 ksi) | 598 MPa (86 ksi) |
| Elongation | 23 % | 27 % |
Recommended Welding Parameters
| Current | TTW Dist. | Voltage | Wire Diameter | Wire Feed Speed |
| 75% Ar - 25% CO2 | ||||
| 130-200 A | 9.5-12.7 mm (3/8-1/2 in.) | 22-26 V | 1.2 mm (.045 in.) | 381-660 cm/min (150-260 in./min) |
| 200-225 A | 12.7-19 mm (1/2-3/4 in.) | 24-27 V | 1.2 mm (.045 in.) | 660-965 cm/min (260-380 in./min) |
| 225-265 A | 19-25.4 mm (3/4-1 in.) | 27-29 V | 1.2 mm (.045 in.) | 965-1321 cm/min (380-520 in./min) |
| 135-250 A | 12.7-16 mm (1/2-5/8 in.) | 22-26 V | 1.4 mm (.052 in.) | 279-584 cm/min (110-230 in./min) |
| 250-295 A | 16-19 mm (5/8-3/4 in.) | 25-29 V | 1.4 mm (.052 in.) | 584-864 cm/min (230-340 in./min) |
| 295-355 A | 19-25.4 mm (3/4-1 in.) | 27-31 V | 1.4 mm (.052 in.) | 864-1194 cm/min (340-470 in./min) |
| 185-285 A | 16-19 mm (5/8-3/4 in.) | 24-28 V | 1.6 mm (1/16 in.) | 279-508 cm/min (110-200 in./min) |
| 285-340 A | 19-25.4 mm (3/4-1 in.) | 27-30 V | 1.6 mm (1/16 in.) | 508-762 cm/min (200-300 in./min) |
| 340-400 A | 25.4-31.75 mm (1-1.25 in.) | 28-32 V | 1.6 mm (1/16 in.) | 762-1067 cm/min (300-420 in./min) |
Deposition Data
| Current | Deposition Rate | Deposition Type | Diameter | Deposition Efficiency (%) | TTW Dist. | Voltage | Wire Feed Speed |
| 150 A | 1.9 kg/h (4.2 lb/h) | 1.2 mm (.045 in.) | 86 % | 28 V | 508 cm/min (200 in./min) | ||
| 210 A | 2.8 kg/h (6.3 lb/h) | 1.2 mm (.045 in.) | 86 % | 29 V | 762 cm/min (300 in./min) | ||
| 250 A | 3.9 kg/h (8.5 lb/h) | 1.2 mm (.045 in.) | 87 % | 30 V | 1016 cm/min (400 in./min) | ||
| 290 A | 4.8 kg/h (10.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 33 V | 1270 cm/min (500 in./min) | ||
| 155 A | 2.0 kg/h (4.4 lb/h) | 1.4 mm (.052 in.) | 87 % | 25 V | 381 cm/min (150 in./min) | ||
| 245 A | 3.3 kg/h (7.3 lb/h) | 1.4 mm (.052 in.) | 86 % | 28 V | 635 cm/min (250 in./min) | ||
| 310 A | 4.6 kg/h (10.2 lb/h) | 1.4 mm (.052 in.) | 85 % | 33 V | 889 cm/min (350 in./min) | ||
| 360 A | 6.0 kg/h (13.3 lb/h) | 1.4 mm (.052 in.) | 85 % | 36 V | 1143 cm/min (450 in./min) | ||
| 190 A | 2.8 kg/h (6.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 27 V | 38 cm/min (150 in./min) | ||
| 300 A | 4.6 kg/h (10.2 lb/h) | 1.6 mm (1/16 in.) | 87 % | 30 V | 35 cm/min (250 in./min) | ||
| 365 A | 5.6 kg/h (12.3 lb/h) | 1.6 mm (1/16 in.) | 86 % | 33 V | 762 cm/min (300 in./min) | ||
| 410 A | 6.4 kg/h (14.0 lb/h) | 1.6 mm (1/16 in.) | 88 % | 33 V | 889 cm/min (350 in./min) | ||
| 75% Ar - 25% CO2 | |||||||
| 130-200 A | Full Range | 1.2 mm (.045 in.) | 9.5-12.7 mm (3/8-1/2 in.) | 22-26 V | 381-660 cm/min (150-260 in./min) | ||
| 200-225 A | Full Range | 1.2 mm (.045 in.) | 12.7-19 mm (1/2-3/4 in.) | 24-27 V | 660-965 cm/min (260-380 in./min) | ||
| 225-265 A | Full Range | 1.2 mm (.045 in.) | 19-25.4 mm (3/4-1 in.) | 27-29 V | 965-1321 cm/min (380-520 in./min) | ||
| 135-250 A | Full Range | 1.4 mm (.052 in.) | 12.7-16 mm (1/2-5/8 in.) | 22-26 V | 279-584 cm/min (110-230 in./min) | ||
| 250-295 A | Full Range | 1.4 mm (.052 in.) | 16-19 mm (5/8-3/4 in.) | 25-29 V | 584-864 cm/min (230-340 in./min) | ||
| 295-355 A | Full Range | 1.4 mm (.052 in.) | 19-25.4 mm (3/4-1 in.) | 27-31 V | 864-1194 cm/min (340-470 in./min) | ||
| 185-285 A | Full Range | 1.6 mm (1/16 in.) | 16-19 mm (5/8-3/4 in.) | 24-28 V | 279-508 cm/min (110-200 in./min) | ||
| 285-340 A | Full Range | 1.6 mm (1/16 in.) | 19-25.4 mm (3/4-1 in.) | 27-30 V | 508-762 cm/min (200-300 in./min) | ||
| 340-400 A | Full Range | 1.6 mm (1/16 in.) | 25.4-31.75 mm (1-1.25 in.) | 28-32 V | 762-1067 cm/min (300-420 in./min) | ||
Classifications
| Classifications | ASME SFA 5.36 : ASME SFA 5.29 : AWS A5.36 : E91T-M21A6-K2H4 AWS A5.29 : E91T1-GM-H4 |
Approvals
| Approvals | ABS QPL-24403/2 MIL-101TM |
| Approvals are based on factory location. Please contact ESAB for more information. |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Mn | Ni | P | S | Si | |||||||||
| 75% Ar - 25% CO2 | ||||||||||||||
| 0.059 % | 1.37 % | 2.09 % | 0.012 % | 0.010 % | 0.36 % | |||||||||