现货供应奥升德PA66 R535H热稳定型增强尼龙66塑胶原料，是一款通用型、热稳定级、35%玻璃纤维增强型PA66树脂，适用于注塑成型应用。该产品是具备优异流动性的本色树脂，保持了PA66材料对多种化学品、机油、溶剂和汽油的出色耐受性，耐防冻液, 耐化学品, 抗疲劳耐久, 耐汽油, 热稳定剂, 高流动性, 含润滑剂, 耐溶剂。适用于汽车发动机进水口，燃油轨，机油模块和滤清器，变速箱侧盖，机油加注管 (OFT)，中冷器端盖，涡轮增压器管路等。
奥升德PA66 R535H物性表：
| Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.41 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 2.00 mm | 0.90 | -- | % | |
Flow : 2.00 mm | 0.40 | -- | % | |
Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 11600 | 8500 | MPa | ISO 527-2 |
Tensile Stress (Break, 23°C) | 210 | 150 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 10500 | 7000 | MPa | ISO 178 |
Flexural Stress (23°C) | 300 | 205 | MPa | ISO 178 |
Poisson's Ratio | 0.40 | -- | ISO 527 | |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 11 | 12 | kJ/m² | |
23°C | 12 | 14 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 70 | 85 | kJ/m² | |
23°C | 80 | 90 | kJ/m² | |
Notched Izod Impact Strength | ISO 180 | |||
-30°C | 11 | 12 | kJ/m² | |
23°C | 12 | 14 | kJ/m² | |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 260 | -- | °C | ISO 75-2/B |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
Melting Temperature | 260 | -- | °C | ISO 11357-3 |
CLTE - Flow (23 to 55°C) | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse (23 to 55°C) | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
RTI Elec | UL 746 | |||
0.750 mm | 140 | -- | °C | |
1.50 mm | 140 | -- | °C | |
3.00 mm | 140 | -- | °C | |
RTI Imp | UL 746 | |||
0.750 mm | 125 | -- | °C | |
1.50 mm | 125 | -- | °C | |
3.00 mm | 125 | -- | °C | |
RTI Str | UL 746 | |||
0.750 mm | 140 | -- | °C | |
1.50 mm | 140 | -- | °C | |
3.00 mm | 140 | -- | °C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
Volume Resistivity (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
Dielectric Strength (1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
Comparative Tracking Index (3.00 mm) | 250 to 399 | -- | V | IEC 60112 |
High Amp Arc Ignition (HAI) | UL 746 | |||
0.750 mm | PLC 0 | -- | ||
1.50 mm | PLC 0 | -- | ||
3.00 mm | PLC 0 | -- | ||
High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
Hot-wire Ignition (HWI) | UL 746 | |||
0.750 mm | PLC 4 | -- | ||
1.50 mm | PLC 3 | -- | ||
3.00 mm | PLC 4 | -- | ||
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
0.750 mm | HB | -- | ||
1.50 mm | HB | -- | ||
3.00 mm | HB | -- | ||
Glow Wire Flammability Index | IEC 60695-2-12 | |||
0.750 mm | 675 | -- | °C | |
1.50 mm | 675 | -- | °C | |
3.00 mm | 675 | -- | °C | |
Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
0.750 mm | 700 | -- | °C | |
1.50 mm | 700 | -- | °C | |
3.00 mm | 700 | -- | °C | |
| Additional Information | Dry | Conditioned | Unit | Test Method |
Automotive Materials - (thickness d = 1mm) | + | -- | FMVSS 302 |
| Processing Information | |||
| Injection | Dry | Unit | |
Drying Temperature | 80.0 | °C | |
Drying Time | 4.0 | hr | |
Suggested Max Regrind | 25 | % | |
Rear Temperature | 280 to 310 | °C | |
Middle Temperature | 280 to 310 | °C | |
Front Temperature | 280 to 310 | °C | |
Nozzle Temperature | 280 to 310 | °C | |
Processing (Melt) Temp | 285 to 305 | °C | |
Mold Temperature | 65.0 to 95.0 | °C | |